The main difference is carbon content. Iron has a carbon content of 2.11 percent or more, while steel has a carbon content of 2.11 percent or less. Iron-carbon alloys with carbon content of more than 2.11% are cast iron (pig iron), which are basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different, and the content of harmful impurities such as sulfur and phosphorus in steel is smaller. Wire general color key, wire color light point, white point.

Galvanized barbed wire (barbed wire) is made of galvanized barbed wire twisted on the main wire, so as to play a protective and isolation role. Among them twist weave way is divided into single twist weave and double twist weave. Construction methods include direct installation and spiral insertion.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

There are many categories of large coils of galvanized wire, and different categories can be applied to different scenarios. Galvanized iron wire common application is the application of the construction industry, one is the use of binding wire, whether it is the binding of scaffolding or reinforcement, need galvanized iron wire to carry out, the common specifications are 22 and 24 wire, common length of 30cm, 35cm, 40cm, 45cm, 50cm. There is also 20kg or 50kg a bundle of 18, 16, 14, 12, 10 galvanized coil wire.

Removal of surface-active substances by activated carbon matting. Or make the bubble unstable according to overworry, these are all reasonable countermeasures; Other strategies should also be used to minimize the amount of surfactant taken in. The introduction of organic matter can make the electroplating process speed drop sharply. Galvanized iron wire blackening can be effectively prevented, such as: the work site to keep dry, reduce and do not use chemicals, operators with clean gloves and so on. In addition, hot dipping zinc factory can be required, after dipping zinc must be passivation treatment, passivation treatment of zinc has a better anti-discoloration effect, can effectively prolong the discoloration time, the combination of the two, discoloration should be able to solve.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

The price of galvanized iron wire performance is the key to win, galvanized wire only with good performance, in order to win the market, in order to obtain customer praise. In galvanized wire, the main function of carbon in increasing hardness, less is less easy to rust, the main function of chromium is acid and alkali resistance; Nickel’s main function is high temperature resistance, acid and alkali resistance and conductive use; The main function of iron is magnetic conductivity; The main functions of titanium are low density, high hardness and strong corrosion resistance. The main function of copper is magnetic and electrical conductivity. Different chemical components have different functions, which together form the characteristics of galvanized wire.