This work confirms previous studies that show P-25 and other untreated anatase 377 nanoparticles should not be employed in sunscreens because the toxicity of P25TiO2NPs under UV radiation is significant.

Natural barite and anthracite containing more than 95% barium sulfate are mixed and fed at a ratio of 3:1 (mass). After being crushed to a diameter of less than 2cm, it enters the reduction furnace. The furnace temperature is controlled to be 1000-1200°C in the front section and 500-500 in the back section. 600°C, the reduction furnace rotates at a speed of 80 seconds per revolution, and the reaction conversion rate is 80% to 90%.

Scrap zinc or concentrated zinc ores are dissolved in sulfuric acid, the solution is purified and the two solutions are reacted. A heavy mixed precipitate results that is 28 to 30% zinc sulfide and 72 to 70% barium sulfate.

Overall, the precipitation of titanium dioxide is a complex process that requires careful control of various factors to achieve the desired product properties. By optimizing the precipitation percentage and carefully monitoring the precipitation process, manufacturers can produce high-quality titanium dioxide that meets the stringent requirements of their customers in the paints, coatings, plastics, and cosmetics industries.

The assessment was conducted following a rigorous methodology and taking into consideration many thousands of studies that have become available since EFSA’s previous assessment in 2016, including new scientific evidence and data on nanoparticles.