The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

Hexagonal net structure can be used for slope support, excavation, rock face net mine support form, slope vegetation (green color), railway road isolation block, it can be made into a cage, pad, used for river, flood dam and seawall erosion protection and reservoir, river closed cage. Driving and guiding rivers and waterlogging disasters are major water erosion damage to rivers, resulting in flooding, resulting in significant loss of property and loss of water and soil. Because of this, in dealing with these problems, the application of the living grid structure becomes a solution plan, which makes it possible to protect the shore forever.

Stainless steel blade barbed rope production process is basically similar to galvanized blade barbed rope production process, usually according to the mold to determine the size of the blade.

Barbed rope is an isolation protective net made of iron wire, which is wound on the main line (twisted wire) through the winding machine and through various weaving processes. Thorn rope generally has three methods of twisting, the following Haorong for you to introduce in detail.

There are many categories of large rolls of galvanized wire, and different categories can be applied to different scenarios. The common application of galvanized iron wire is the application of the construction industry. One is the use of binding wire. Whether it is the binding of scaffolding or reinforcement, galvanized iron wire is needed to carry out. There are also 20kg or 50kg bundles of No. 18, No. 16, No. 14, No. 12, No. 10 galvanized coils.

In order to make the zinc content of steel wire stable in the future, and maintain its uniformity, as far as possible to reduce the zinc content, and effectively reduce zinc consumption to the actual work, the following measures are proposed by the wire factory:

The large roll of galvanized silk should be coated with oil, the fiber core is dipped in oil, and the grease should be able to protect the fiber core from decay and corrosion, the iron wire moistens the fiber, and lubricates the wire rope from the inside. The surface is coated with oil so that all the wire surface in the rope strand is evenly coated with a layer of anti-rust lubricating grease, which is used for the mine rope with friction lifting and mineral water, to be coated with black grease with increased wear and strong water resistance. Other uses are coated with red oil oil with strong film and good rust resistance, and require it to have a thin oil layer, which is easy to keep clean during the operation.