Now most people want to choose a few when choosing barbed wire material better thorn rope, but the special barbed wire the better, not right, it is important to choose which model is most suited to their own thorn rope,, although is very simple product, but in the use of these products are for specific situation is different, and has a different effect, Maybe now consumers do not have too much concept of blade barbed rope, in fact, such barbed rope products have a higher safety factor. In addition, there are also more and more barbed rope, dazzling reasons, here is an example to illustrate the choice of special barbed rope.

Compared with other galvanizing processes, galvanized steel wire has low cleaning requirements before plating. However, under the current trend of increasing the quality level of galvanized layer, some pollutants brought into the plating tank are obviously harmful. Because cleaning galvanized coating wastes a lot of time and reduces production, it is very important to properly clean and effectively rinse the substrate before electroplating.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

4,  galvanized can be used zincate galvanized or chloride galvanized process, should use appropriate additives to meet the requirements of this standard coating.

Many electrogalvanized wire diameter products are formed by wire drawing, wire drawing is a kind of processing technology, can make the product reach the required shape and meet the standard mechanical properties. Cold wire drawing is carried out at recrystallization temperature, hot wire drawing is carried out at crystallization temperature, warm wire drawing is drawn at higher than room temperature and lower than crystallization temperature. Cold drawing is a common drawing method.