Certificate of Analysis (Lithopone B301, Lithopone B311 powder TDS)
Does not work with hydrogen sulfide and alkaline solutions. It is easy to decompose in the presence of acid to produce hydrogen sulfide gas. It is easily oxidized in the air and deteriorates after moisture. Whiteness and hiding power are strong.
The natural barite containing more than 95% of barium sulfate is mixed with anthracite in a ratio of 3:1 (mass), and is pulverized to a diameter of about 2 cm or less to enter a reduction furnace, and the front stage of the furnace temperature is controlled by 1000 to 1200 ° C, and the latter stage is 500 to 600 ° C, the reduction furnace rotates at a speed of 80s per revolution, the reaction conversion rate is 80% to 90%, the obtained barium sulfide enters the leaching device, the control temperature is above 65 ° C, and the content of barium sulfide is 701%, and then enters the clarification. The barrel is clarified and then added with zinc sulfate to control the zinc sulfate content to be greater than 28%, and the pH is 8-9, and a mixture of barium sulfate and zinc sulfide having a density of
Titanium dioxide used for adhesive applications should contain an inorganic coating to control polarity, improve its ease of dispersion, and improve its weather resistance. The inorganic coating (zirconium dioxide, silica, alumina) is applied in the aqueous slurry by precipitation of one or more hydrated metal oxides and by neutralization of acidic and alkaline compounds.
Lithopone is produced by coprecipitation of barium sulfate and zinc sulfide. Most commonly coprecipitation is effected by combining equimolar amounts of zinc sulfate and barium sulfide:
Scientists analyzed research that examined how titanium dioxide nanoparticles interact with the brain for a 2015 review published in Nanoscale Research Letters. The researchers wrote: “Once the TiO2 NPs are translocated into the central nervous system through [certain] pathways, they may accumulate in the brain regions. For their slow elimination rates, those NPs could remain in the brain zones for a long period, and the Ti contents would gradually increase with repeated exposure.” After reviewing dozens of studies, the scientists concluded: “Long-term or chronic exposure to TiO2 nanoparticles could potentially lead to the gradually increased Ti contents in the brain, which may eventually induce impairments on the neurons and glial cells and lead to CNS dysfunction as a consequence.”