The properties of lithopone are very suitable for use in the production of coatings. Because the ingredients of lithopone are zinc sulfide and barium sulfate, and the more zinc sulfide content, the stronger its covering power. This indicates a paint product with strong white covering power. It is different from water in that it reacts with acid but does not react with alkali. It has a wide range of uses. Because its structural properties are similar to titanium dioxide and its price is relatively cheap, it can also be used as a substitute for some titanium dioxide. Lithopone can be used for coloring paints, inks, pigments, rubber, paper, leather, enamel, etc.

...

2. The preparation of the lining powder: The above-mentioned final immersion liquid 1000 ml in a 2000 ml beaker, heated to 98 ° C, and then added 4 g of ammonium persulfate with a magnetic stirrer stirring 0. 5h, after the oxidation of the solution, adding polyacrylamide 02%。 The solution, the volume of the solution is 0.02%. After lh filtration, the obtained filtrate is subjected to sulfurization and impurity removal, and zinc powder is substituted to obtain a zinc sulfate ammonia refining complex liquid. 122. 9g of antimony sulfide (without water) and 21. 7g of sodium sulfide (without water) are mixed and dissolved in distilled water to obtain a metathesis reaction solution, and a nonionic surfactant 0P-10 (for nonylphenol and epoxy) is added to the solution. The condensate of acetamidine) 0. 2g, the reaction temperature is 40 ° C, the stirring speed is 15m / s, stir well for 40min, then slowly added to 1000ml zinc sulfate ammonia refining complex, continue to stir for 30min and then add quality The fractionation is 30% 3⁄40 2 of desulfurization bleaching, and after bleaching, the nZnS-BaS0 4 crystal filter cake is separated by filtration.

...
...

Having thus described the origin and uses of the pigment, we now come to the question, what is lithopone? It is, in short, a chemical compound usually consisting of 30.5 per cent zinc sulphide, 1.5 per cent zinc oxide and 68 per cent barium sulphate, but these proportions vary slightly in the different makes. Lithopone of this composition is sold as the highest grade, either as red seal or green seal, as it best suits the idea of the manufacturer. Many manufacturers, especially in Europe, sell and also export other brands under other seals, containing 24, 20, 18 and as little as 12 per cent of zinc sulphide with very small percentages of zinc oxide, the balance being usually barium sulphate, but sometimes certain portions of China clay or gypsum (calcium sulphate) or whiting (calcium carbonate). Such brands are not a chemical compound, but mechanical mixtures of the chemically compounded lithopone and the admixtures referred to.

...