In order to contribute with experimental evidence that could help to achieve a better understanding of the field for future regulation, in the present work, the biocompatibility of commercial P25TiO₂NPs (one type of TiO₂NPs used in sunscreen formulations) and two novel functionalized P25TiO₂NPs were evaluated under solar simulated irradiation. White light, generated by red, blue, and yellow LEDs, together with UV ones, was chosen to simulate the solar spectra. Functionalization of TiO₂NPs was made with antioxidant vitamins in order to prevent the expected photo-initiated ROS production when nanoparticles are exposed to the simulated solar spectra. Vitamin B2 (riboflavin) and vitamin C were chosen to carry out the functionalization because they are water-soluble, low-cost, and are a constitutive part of biological processes. In addition, it is known that both have the potential to prevent macromolecular oxidation by ROS [23], [24], [25], [26].

In 1970, Japanese scholars studied the phase diagram of iron oxide microcrystalline formation, which laid a theoretical foundation for the preparation method of iron oxide yellow crystal seed. According to the research results, iron yellow crystal seeds can be formed under acidic or alkaline conditions. Because iron yellow is a crystal structure, in order to crystallize into pigment particles, it must first form crystal nucleus and become crystal seed, and then the crystal nucleus grows into iron yellow. Otherwise, only thin and dim color paste can be obtained, which does not have pigment properties. Acid process can be divided into iron sheet process and drop addition process.