As early as sixty years ago, zinc sulphide was first thought of as a pigment for coloring India rubber and a patent for the process of its manufacture was issued in England. But it was not until twenty years later that zinc sulphide and its manufacture was seriously considered as a pigment for paint, and in 1874 a patent was issued for a process of manufacturing a white pigment, composed of zinc sulphide and barium sulphate, known as Charlton white, also as Orr's white enamel. This was followed in 1876 by a patent issued to a manufacturer named Griffith and the product, which was similar in character to Charlton white, was known as Griffith's patent zinc white. In 1879 another patent for a more novel process was obtained by Griffith & Cawley, the product made under this process proving the best of the series placed upon the market up to that date. After that time many new processes were patented, all, however, tending to the same object, that of producing a white pigment, composed of zinc sulphide and barium carbonate, the results, however, in many cases ending with failure.

Natural barite and anthracite containing more than 95% barium sulfate are mixed and fed at a ratio of 3:1 (mass). After being crushed to a diameter of less than 2cm, it enters the reduction furnace. The furnace temperature is controlled to be 1000-1200°C in the front section and 500-500 in the back section. 600°C, the reduction furnace rotates at a speed of 80 seconds per revolution, and the reaction conversion rate is 80% to 90%.