Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.

Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.