1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Stainless steel hexagonal network is composed of machine will be produced stainless steel wire of a kind of metal mesh, not easy corrosion, the survival of the fixed number of year is longer, net of wide, coarser size, strong practicability, flexibility and other unique places, stainless steel hexagonal wire netting material is stainless steel wire, wire diameter because stainless steel wire big viscosity of large stainless steel hexagonal network would be hard to manufacture, Of course, it is more difficult to hold the edge or twist the edge, so stainless steel hexagonal mesh whether from the material or artificial are expensive, but stainless steel hexagonal mesh will not rust and use years is also very long, appearance without disposal can achieve the use effect.

Wire mesh production of general selection of low carbon wire, after fine and accurate active welding equipment processing, the selection of galvanized process surface treatment. After the completion of the product, the net surface is smooth and regular, good integrity, strong and consolidated, even if part of the choice or pressure will not appear lax phenomenon.

Advantages: The cost of hot dip galvanized rust prevention is lower than that of other paint coating. In suburban environment, the standard hot-dip galvanized rust prevention thickness can adhere to more than 50 years without repair. In urban or offshore areas, the standard hot-dip galvanized rust protection layer can last 20 years without repair. Galvanized layer and steel is a metallurgical connection, into a part of the steel surface, so the durability of the coating is more reliable.

Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is to use the lead screw above the zinc pot, the length of the distance to the ceramic sinking roller. Thick wire diameter zinc dipping time should be long, fine wire diameter zinc dipping time should be short, zinc dipping length is in the range of 2~3.5m, which is also to reduce the zinc consumption of steel wire, is an aspect of maintaining the uniformity of zinc layer.

The main difference between the two is the carbon content. The carbon content of iron is 2.11 percent or greater, while the carbon content of steel is 2.11 percent or less. The iron carbon alloy with carbon content above 2.11% is cast iron (pig iron), which is basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different. The content of harmful impurities such as sulfur and phosphorus in steel is smaller. Steel wire general color focus, iron wire color light point, white point.