Cold wire drawing is a kind of cold processing of metal, that is, we often say reinforcement. Cold drawing process is not messy, cold drawing price based on the quality of cold drawing dividends of different levels, cold drawing production is also a variety of different procedures. The main factor affecting the strength of cold drawing wire is raw materials, which are closely related to the raw materials, strength and diameter of raw materials, and the better the quality of cold drawing wire, the more messy the production process.

High quality galvanized wire in general, the zinc layer attached to the surface of the wire is relatively thick, so when we buy galvanized wire, as long as we look at the thickness of the zinc layer machine, we can generally judge whether the quality of galvanized wire is high quality.

2. The cleaning agent used for cleaning should have no effect on the binding force of the coating and no corrosion on the matrix.

Hot dip galvanized wire is used in carbon structural steel, which is processed by drawing and hot dip galvanized. It is widely used in the manufacture of wire mesh, highway guardrail and construction projects. Electro galvanized wire is a kind of metal conforming material made of low carbon steel as core wire by wire drawing and electro galvanized process. Mainly used in wire mesh, highway guardrail and construction projects.

Spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and resistance to impact and oscillation. The strength and endurance objectives, especially to prevent the occurrence of modification cracks, are the key to the consumption of spring wire. The inner quality and outer quality of the wire rod directly affect the function of the wire.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

2. The cleaning agent used for cleaning should have no effect on the binding force of the coating and no corrosion on the matrix.