Large coil galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling process and other processing. Galvanized wire is divided into hot galvanized wire and cold galvanized wire. Galvanized wire in the process of smelting there are a lot of need to pay more attention to the place, galvanized wire products in the manufacturing process will experience a lot of process, of which the following galvanized wire annealing is a very important step, this step to the nature of galvanized wire has brought a lot of help.

Moderate rates of foam formation may be harmless. The presence of small, homogeneous particles of large denier in the tank can stabilize the foam layer, but the accumulation of excessive solid particles can cause an explosion.

The common weight standard of galvanized barbed rope is 25kg per coil, and the length of each coil varies from 220-250 meters according to the specifications of the barbed rope. And of course we all know that the heavier the disc the longer it is. But there is one point that is worth our attention, that is, the hollow inside the general larger disk is relatively small, and the hollow inside the lighter galvanized thorn rope is relatively large. The purpose of this is to reduce the number of bending of the thorn rope and make it easier and more beautiful when installing, on the other hand, it looks larger in appearance.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.