When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

With the improvement of people’s living standards now, many families are keeping some small pets, these small pets also need a stable nest, pet cage has become a more important choice of people, each pet habits and living habits will choose to adapt to the cage.

The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.

Hardness is a commonly used property index in mechanical properties of metal materials. The iron wire factory introduces a fast and economical test method for hardness testing. However, for the hardness of metal materials, there is not a unified and clear definition including all test methods at home and abroad. In general, the hardness of a metal is often considered to be the resistance of the material to plastic deformation, scratches, wear, or cutting.

According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

Now most people buy barbed rope choose blade barbed rope, why is this? The blade gill net is made of hot-dip galvanized steel plate or stainless steel sheet to punch out sharp knife sheets. The high tension galvanized steel wire or blade barbed wire is made of stainless steel wire as the core wire. Because the gill net shape is not easy to contact, so it can reach excellent protection barrier effect. The primary raw materials of the product are galvanized sheet and stainless steel plate.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

Some customers pay more attention to the quality problem, so they pay more attention to the service life. The barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.