Pet cage is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welding, its characteristics are beautiful, light, folding, easy to store. Pet cage surface treatment is generally: cold galvanizing, hot galvanizing, spraying, dipping, chrome plating, nickel plating and other methods. Pet cage is mainly used for family breeding pets and protection. Tianfu metal products company specializes in the production of various specifications of pet cage such as pigeon cage, dog cage, bird cage, parrot cage and so on.

At present, there are two processing methods of blade stabbing rope. One is to make it into a spiral shape, and then make a clip treatment. It is not only our common spiral blade stabbing rope, but also a single spiral blade stabbing rope without clip, but even a single helix can not stretch it to a relatively straight. This is mainly because the blade barbed rope is wrapped and wound at the same time, so it can only be spiral.

1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

PVC coated barbed rope is widely used for railway highway protection, but also for safety protection of rivers, embankments and seawalls, so as to better protect the safety of people and animals.

Unless it is a specially customized model, the stainless steel blade barbed rope produced now is generally produced with a 22mm blade length mold, which is what we usually call bto-22 type. It doesn’t have to be the case that there are specifications from 11mm to 65mm. Unless the customer insists on customizing the specified length, the barbed rope manufacturer produces bto-22 stainless steel blade barbed rope.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.

The use of electric welding mesh is very wide, can be used in many places. In the field of construction, especially the wall crack, has played a very important role, the traditional construction, is to put on mortar directly onto the wall, after such a long time, will appear fall off and fracture phenomenon, in order to prevent the occurrence of this phenomenon, must use welded wire mesh before rendering, welded wire mesh is fixed to the wall, above the plastering construction, Can ensure that the wall level for a long time, not easy to crack phenomenon.