No matter how good the quality of hot-dip galvanized barbed rope is, it is only attached to the surface of the wire with galvanized layer, and with the cause of chemical reaction, the zinc layer on the surface will gradually lose its effect because of oxidation reaction, which is more prominent in the humid area of the environment. And because, after all, the wire will rust, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.

The external environment has a great influence on the storage of cold drawn wire. Especially during the rainy season, special attention should be paid to the air humidity of workshops and warehouses. It is recommended to use moisture test paper with a value between 8 and 10. If the PH value is high, attention should be paid to the corrosion of the internal cold drawing wire. Cold drawing wire in normal environment storage for two years no problem, cold drawing wire will not be corroded. However, it is necessary to place the coil gently during the handling process to avoid the winding position leading to the cable is not smooth.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

Unless it is a specially customized model, the stainless steel blade barbed rope produced now is generally produced with a 22mm blade length mold, which is what we usually call bto-22 type. It doesn’t have to be the case that there are specifications from 11mm to 65mm. Unless the customer insists on customizing the specified length, the barbed rope manufacturer produces bto-22 stainless steel blade barbed rope.

The main difference between the two is the carbon content. The carbon content of iron is 2.11 percent or greater, while the carbon content of steel is 2.11 percent or less. The iron carbon alloy with carbon content above 2.11% is cast iron (pig iron), which is basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different. The content of harmful impurities such as sulfur and phosphorus in steel is smaller. Steel wire general color focus, iron wire color light point, white point.

Some customers may not immediately use the blade barbed rope when they buy it for retail and some are temporarily not used for site construction. At this time, customers need to follow up the characteristics of the blade barbed rope for storage. Because they are afraid of the rain, so there is no need to say more, and the surface of the packaging is more afraid of the sun, so it is not recommended to prevent the outside of the blade thorn rope will lead to the woven bag become lost effect, resulting in the exposure of the internal blade thorn rope affect the later use.

The production process of stainless steel blade and galvanized blade is basically similar. The blade size is usually determined according to the mold.