properties lithopone manufacturer
...
2025-08-14 17:00
525
2. Barite calcination method A solution of barium sulfide is prepared. The sulfuric acid and zinc oxide are reacted, purified by adding potassium permanganate and zinc powder, and compressed to obtain a zinc sulfate solution. Then, the prepared barium sulfide solution is mixed and subjected to a metathesis reaction to obtain a mixture of zinc sulfide and barium sulfate, and then the precipitate is subjected to pressure filtration, calcination, wet grinding, drying, and pulverization to obtain a zinc white product.
...
2025-08-14 16:31
1842
Application:
1. Due to its rheological and optical properties, Lithopone offers technical and economic advantages wherever organic and inorganic resin systems need to be relatively highly pigmented for specific applications. Lithopone has therefore traditionally been used in putties, mastics, jointing and sealing compounds, primers, undercoats and marking paints. In powder coatings it is possible to replace TiO2 partially, very economically.
2. The low Mohs' hardness of Lithopone leads to low abrasiveness in comparison with TiO2.
3. Lithopone 30 % (= 30% zinc sulfide share) is proven to be of particular use as a TiO2 Substitute in thermoplastic masterbatches. Even at very high pigment loadings it disperses easily. A masterbatch containing 50 % TiO2 and 25 % Lithopone 30 % DS has the same hiding power as one containing 60 %TiO2. Cost savings are strongly related to the price ratio of Lithopone and TiO2 and the price of for example polyethylene or polypropylene.
4. The Lithopone batch has a much higher extrusion rate too. Furthermore the impact strength of many thermoplastics such as PP and ABS can be noticeably improved by using Lithopone as a TiO2 substitute. Generally spoken, Lithopone can be used at loadings up to 80 % by weight without causing polymer breakdown
...