2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

The characteristics of galvanized hexagonal net: easy to use; Save transportation costs. It can be shrunk into small rolls and involved in moisture-proof paper packaging, taking up little space. Coating thickness uniformity, stronger corrosion resistance; The construction is simple and does not require special technology; Strong resistance to natural damage and corrosion resistance and adverse weather effects; Can withstand a large range of deformation, and still not collapse. It has the function of fixed heat preservation and insulation.

The derusting steel parts are immersed in the melted zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to achieve the purpose of anti-corrosion. The surface of galvanized wire coating can see whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire.

The protective duration of the galvanized layer of large roll galvanized wire is closely related to the thickness of the coating. Generally speaking, in relatively dry main gas and indoor use, and in harsh environmental conditions, the thickness of galvanized layer needs to be very high. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance.