The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

There is a connection between the hook mesh and the aperture, in short, the general hole small hook mesh, the wire is also very small; Aperture is large, hook mesh wire is generally larger. The weaving of the hook mesh also has certain rules, using the first pre-bent into a wavy wire, and then woven into the hook mesh. According to the knitting method, the hook mesh can be divided into: closed weaving, two-way plain weaving, one-way corrugated weaving, two-way plane weaving, two-way corrugated weaving, rectangular hole weaving.

In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.

This process has no mold, low processing cost, easy forming, can process a variety of shapes and other characteristics are widely used. But the products of the guardrail are powder impregnated plastic. According to whether it needs heating, it is divided into hot dipping and cold dipping. According to the raw materials of dipping, it can be divided into liquid dipping and powder dipping. Hot-dip galvanizing, as a metal anticorrosion method, is usually to put the steel structure to be derusted into the zinc liquid at about 500℃, so that the zinc layer is attached to the surface of the steel structure.