Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

Stainless steel blade barbed wire production process is similar to galvanized blade barbed wire production process, usually according to the mold to determine the size of the blade.

Compared with the traditional protective device, the advantages of barbed wire protective net are very obvious. First of all, because of the standardized production mode, the barbed wire net is dense after installation. Not conducive to the passage of personnel. The traditional way of protection due to private disorderly construction of the density of the protective net can not play a protective performance. So the installation of barbed wire net is the best choice to protect the home.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Galvanized iron wire is selected from excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process: