Natural barite and anthracite containing more than 95% barium sulfate are mixed and fed at a ratio of 3:1 (mass). After being crushed to a diameter of less than 2cm, it enters the reduction furnace. The furnace temperature is controlled to be 1000-1200°C in the front section and 500-500 in the back section. 600°C, the reduction furnace rotates at a speed of 80 seconds per revolution, and the reaction conversion rate is 80% to 90%.

lithopone supplier 30% increases extruder performance and reduces processing costs, improves quality and is suitable for masterbatch for injection of Polyolefins, ABS, Polycarbonate, Polypropylene, Polyethylene, Polystyrene, single layer films, multi-layer films and for white, coloured and filled masterbatch. The combination of lithopone supplier 30 with TiO2 results in improved mechanical properties including higher elongation values and better impact resistance.