In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

The price of galvanized iron wire is relatively low, but the corrosion resistance is excellent, so it is favored by many screen businesses. In the production process of galvanized iron wire, first of all, we should check the equipment to see if there are any problems, and then we should look at the galvanized process, whether there are factors that cause product discoloration. If these problems do not exist, or some of them occur on the same equipment, and some are normal, then we should consider the problem of raw materials at this time.

Large rolls of galvanized silk play a very important role in our life. Made of low carbon steel rod processing, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance.

Open pit coal mine due to poor air quality, a variety of harmful heavy metals are also more, so the corrosion strength of barbed rope products is particularly large, when using galvanized barbed rope must choose hot plating or plastic coated galvanized barbed rope, although the price is slightly higher, but in the long term development is more appropriate. Besides, when the barbed rope is installed near the coal mine, the pile foundation should be fixed to prevent the barbed rope from falling down due to soil erosion, thus losing the protective effect.

The barbed rope produced by the barbed rope factory adopts the way of winding in order to facilitate transportation, and the disk weight of the galvanized barbed rope is different according to the size.

Bridge protection system generally do not need to install special drainage system, the use of hexagonal mesh gabion cage, the filling is selected stones, the stones are not easy to wear, and between the stones and stones will retain some space, so it is very good to meet the drainage requirements.

Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.

Most cattle nets are mechanically woven from high ductibility and corrosion resistant low carbon steel wire or PVC coated steel wire. The manufacture of cattle net several common raw materials are generally galvanized wire, hot dip galvanized wire, galfan steel wire plating, ten percent aluminum zinc alloy steel wire and the new selenium chromium wire plating.

The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

1, must often clean and scrub the stainless steel pet cage, keep the surface of the stainless steel pet cage clean, dry, can ensure the stainless steel pet cage bright every day.