The morphology of vitaminB2@P25TiO₂NPs is coherent with the description of Degussa P25 typical population. Size distribution histograms were made from manual measures of the nanoparticles observed in SEM micrographs using ImageJ®. This data showed that more than 70% is anatase (between 20 and 60 nm) with a minor amount of rutile characteristic bars (between 80 and 100 nm) and a small amount of amorphous phase (<40 nm) [36]. Further analysis of the same sample areas with an EDS probe demonstrated the presence of organic material composed of C and O (Fig. 2). This material was found homogeneously distributed on the surface of the different shapes of P25TiO₂NP, not in the background, indicating a specific interaction that could be attributed to the functionalization of the P25TiO₂NPs with vitamin B2.