One of the main benefits of using titanium dioxide in paint is its excellent hiding power. It allows the paint to effectively cover the surface, hiding imperfections underneath. This produces a smooth, even surface that gives walls a flawless appearance. Whether you're hiding stains or uneven patches, titanium dioxide-infused paint ensures a seamless and professional look.
Scrap zinc or concentrated zinc ores are dissolved in sulfuric acid, the solution is purified, and the two solutions are reacted. A heavy mixed precipitate results that is 28 to 30% zinc sulfide and 72 to 70% barium sulfate.
Below 20% substitution, it is recommended to replace 1 kg of TiO2 with 1 kg of Lithopone.
Natural barite and anthracite containing more than 95% barium sulfate are mixed and fed at a ratio of 3:1 (mass). After being crushed to a diameter of less than 2cm, it enters the reduction furnace. The furnace temperature is controlled to be 1000-1200°C in the front section and 500-500 in the back section. 600°C, the reduction furnace rotates at a speed of 80 seconds per revolution, and the reaction conversion rate is 80% to 90%.