When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well. Galvanized wire, also known as hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.