Application of lithopone in rubber and plastics application of lithopone in plastics and pigments lithopone can whiten and improve the compressive strength of products. Lithopone is easy to disperse rapidly, and thus the production process of this product is convenient, especially the molding, injection molding and actual operation process. It is worth mentioning that, with its organic chemical plasticity, it can also be integrated into the vulcanized rubber effect of recycled rubber.
Lithopone’s historical significance is further accentuated by the advancements and modifications that followed its inception. The 1874 patent by J.B. Orr, for instance, ushered in a new white pigment—Orr’s Zinc White. This innovation was attained by co-precipitating zinc sulfate and barium sulfide, followed by a calcination process. Further refinements marked the subsequent decades, the most notable being the enhancement of lightfastness achieved in the 1920s by introducing small amounts of cobalt salts before calcination.
Lithopone B301, Lithopone B311 powder, brilliant white pigment used in paints, inks, leather, paper, linoleum, and face powder. It was developed in the 1870s as a substitute or supplement for lead carbonate (white lead), to overcome its drawbacks of toxicity, poor weathering, and darkening in atmospheres that contain sulfur compounds. Lithopone B301, Lithopone B311 powder is an insoluble mixture of barium sulfate and zinc sulfide that precipitates upon mixing solutions of barium sulfide and zinc sulfate. The precipitate is recovered by filtration, then calcined (roasted) at temperatures above 600° C (1,112° F). Although Lithopone B301, Lithopone B311 powder has been replaced in many applications by titanium dioxide, it is still widely used in a number of products, such as water paints.
Polyvinyl Butyral Resin (PVB) is a solvent Resin synthesized by the acetal reaction of Polyvinyl Alcohol (PVA) and butyraldehyde in contact with coal.
Because Pvb Resin itself contains a lot of hydroxyl groups, it can bridge with some thermosetting resins to improve the properties of chemicals and film hardness.
Because PVB resin has the above excellent characteristics, it is widely used in adhesive safety glass intermediate film of automobile and building, rust cutting primer, baking paint, wood paint, printing ink, adhesive of electronic ceramics and printed circuit board, adhesive between metal and metal, between metal and plastic, modifier of hot-melt adhesive, iron dimension waterproof processing of textile, etc. A variety of new industrial applications are also continuously developed and applied.
The general characteristics of PVB are as follows:
The appearance of polyvinyl butyral (PVB) resin is white spherical porous particles or powder, and its specific gravity is 1:1; However, the filling density is only 0.20 ~ 0.35g/ml.
Thermal properties
The glass transfer temperature (TG) of polyvinyl butyral (PVB) resin ranges from 50 ℃ of low degree of recombination to 90 ℃ of high degree of recombination; The glass transfer temperature can also be adjusted by adding an appropriate amount of Plasticizer to reduce it below 10 ℃.
Mechanical properties
The coating of polyvinyl butyral (PVB) resin has good water resistance, water resistance and oil resistance (it is resistant to aliphatic, mineral, animal and vegetable oils, but not to sesame oil). PVB is widely used in printing inks and coatings because it contains high hydroxyl groups and has good dispersibility to pigments.
In addition, its chemical structure contains both hydrophobic acetal and acetic ACID groups and hydrophilic hydroxyl groups, so PVB has good adhesion to glass, metal, plastic, leather and wood.
Chemical reaction
Any chemical that can react with secondary alcohol will also react with PVB. Therefore, in many applications of PVB, it is often used with thermosetting resin to bridge and harden with the hydroxyl group of PVB, so as to achieve the characteristics of chemical resistance, solvent resistance and water resistance.
Of course, films with different characteristics (such as hardness, toughness, impact resistance, etc.) can be prepared according to different types of thermosetting resin and different mixing ratio with PVB.