Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.

The number of each bundle of the blade barbed rope is 50, which is reduced by hydraulic compression and thus more convenient for loading and unloading. The forklift can load and unload easily. Under normal circumstances, when the export will be packaged and sold, so that the volume occupied in the container is relatively small, it can be easily placed and will not take up much space.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

Greenhouse steel pipe is mainly made of greenhouse composite materials made of pull rod, pressure rod, column, and arch rod to cover the plastic film in a greenhouse. Wire factory introduces its this shape is circular plastic greenhouse, this greenhouse covers a large area, the effect of heat absorption is also very good, convenient to build, the cost of building a is also very low. The raw material source of greenhouse steel pipe is very rich and extensive, and the application effect is good.

Any application environment, users want a better the strength of the welded wire mesh, only need to improve its intensity, will make better the habit of using demand, but to be improved in the strength of this product, also need yo have a variety of conditions, will need to see factory in produce what kind of material, the strength of the product also is the material strength, But a manufacturer in the data does not fit the strength requirements, after all, there is no way to make the strength of the product progress, so this is the condition to.

There are still some differences between electric mesh and wire mesh and steel mesh. This mesh is mainly a welding mesh made of high quality low carbon steel wire after straightening and cutting, and then welded by electric welding equipment. It can be said that because of the characteristics of fast production and convenient transportation, it has been applied in many industries. In today’s construction projects, people can also see the image of this network well. The application of welded mesh in this industry is mentioned because of its strong corrosion resistance and uniform mesh. It has become a special grid for floor heating in construction industry and has been applied in many fields.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

When galvanized wire is galvanized, it is generally necessary to pay attention to the following problems: the duration of the protective effect of galvanized wire is greatly related to the thickness of the coating. Generally speaking, in the dry main gas and in indoor use, the thickness of galvanized wire galvanized layer only 6-12 μm “, and in harsh environmental conditions, galvanized wire galvanized layer thickness needs 20μm “to B height up to 50μm”. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire.

The derusting steel parts are immersed in the melted zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to achieve the purpose of anti-corrosion. The surface of galvanized wire coating can see whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire.