The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.

Bridge protection system generally do not need to be specially installed special drainage system, the use of hexagonal mesh made of gabion mesh box, the inside of the filler are selected stones, these stones are not easy to wear, and between the stones and stones will retain some gaps, so it is very good to meet the drainage requirements.

Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

Now many hardware manufacturers produce iron wire, and iron wire is very easy to rust, if you need to use in outdoor or humid places, generally customers will require the use of galvanized iron wire equipment to give the wire a layer of zinc, the thickness can be determined according to user requirements. Galvanized iron wire equipment is specially used for the plating of iron. Generally speaking, the stability of zinc is much higher than that of iron, and it will not rust in the daily water vapor or damp place.