Now large roll galvanized wire in our life the use of more and more, to galvanized wire products bring a great market, galvanized wire products are more and more types. The surface coating of good quality galvanized wire is continuous and smooth. When the plating parts are installed and combined, there can be no flow hanging, slag or drop remaining, and no surface defects such as iron exposure. Good quality galvanized wire, coating must be uniform, roughly uniform in copper sulfate solution soaking five times without exposing iron. And with hammering test does not bulge, do not fall off. This is a good galvanized wire should have characteristics.

With the improvement of people’s living standards, now many families are raising some small pets, these small pets need a stable nest, pet cage has become a more important choice of people, each pet habits and living habits will choose to adapt to the cage.

The derusting steel parts are immersed in the melted zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to achieve the purpose of anti-corrosion. The surface of galvanized wire coating can see whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire.

Stainless steel blade barbed rope production process is basically similar to galvanized blade barbed rope production process, usually according to the mold to determine the size of the blade.

Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.

Cold wire drawing is a kind of cold processing of metal. The raw material is wire rod, which is produced by peeling, galvanizing and other processes. Galvanized cold drawing is used more in building materials. Its testing standards are also different. The strength of cold drawing is relatively high. Because of the high strength of steel, it plays a very important role in construction. It saves the construction steel in building materials, and also reduces the cost of the project. It also plays a very important role in the structure of concrete.

The quality of hot-dip galvanized barbed wire is only in the surface of the wire attached to the galvanized layer, and with the reason of the chemical reaction, the surface of the zinc layer will gradually lose its role because of the oxidation reaction, this situation is more prominent in humid areas. And because after all, the steel wire will rust, so the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.