The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

Now it is mainly 12 or 14 galvanized barbed rope. Although they are calculated according to the price per ton, the calculation is different when it comes to every meter, because the thickness of the silk is not the same, which causes the problem that one galvanized barbed rope of equal weight is longer and the other is longer. Customers must have detailed communication with the barbed rope factory before purchasing to avoid such problems.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

Titanium alloy with low carbon content is obtained because the carbon content remains the original concentration. The hardness of titanium alloy is mainly related to its carbon content. Therefore, after carburizing and subsequent heat treatment, the workpiece can obtain the performance of hard and tough inside. Galvanized wire varieties are mainly classified into three categories: electric galvanized wire, hot galvanized wire and galvanized wire. Among them, the classification of galvanized wire is divided into large roll galvanized wire, medium roll galvanized wire, small roll galvanized wire, galvanized shaft wire, truncated galvanized wire and other main production varieties.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

The advantage of galvanized iron wire after annealing: after annealing increases the elongation of the iron wire. Makes the product softer and increases the range of application. After electric galvanizing hot dip galvanizing. Copper electroplating is widely used and screen production. Galvanized iron wire is a soft iron wire product processed by low carbon steel wire through cold drawing, heating, constant temperature, and even heat preservation. Generally, the quality of ordinary galvanized iron wire will be relatively soft, the softness is relatively balanced, and the color is consistent. It is mainly used in construction, mining, chemical industry and so on.