Lithopone is produced by coprecipitation of barium sulfate and zinc sulfide. Most commonly coprecipitation is effected by combining equimolar amounts of zinc sulfate and barium sulfide:

Safety

1. 296 to 1.357 g/cm3 is obtained. The reaction solution is subjected to pressure filtration through a plate frame to obtain a cake-like lithopone powder having a water content of not more than 45%. The mixture is calcined in a dry roaster to change the crystal form of the lithopone, and then acid-washed with sulfuric acid at a temperature of 80 °C. Finally, it is washed with water, reinforced with coloring agent, pressure filtration, drying and milling.

Moreover, titanium dioxide is also used in rubber formulations to improve the processing and curing properties of rubber compounds. It acts as a catalyst in the vulcanization process, speeding up the cross-linking of rubber molecules and enhancing the overall performance of the final product. This results in rubber products that are stronger, more flexible, and better suited for a wide range of applications.