Polyvinyl butyral (PVB) is dissolved into 12 ~ 14% solution with ethanol and made into film. It is used for printing paper film of ceramic (or enamel) products. The fired ceramic (or enamel) patterns have bright color and smooth texture. The flower paper is characterized by convenient use, low cost, smaller than the original glue, greatly reducing the decal process and high color burning rate. At present, most porcelain factories in China have formed relatively formal production lines for standardized production. Therefore, the demand for PVB in the ceramic (or enamel) flower paper industry is increasing.
Application field of polyvinyl butyral -- electronic adhesive
Polyvinyl butyral contains hydroxyl, vinyl acetate and butyraldehyde, which has high bonding properties. Phenolic Resin was added into PVB ethanol solution to make adhesive, which can be used for a long time at 120 ℃. The product has strong adhesion to metal, wood, leather, glass, fiber and ceramics; FRP can be manufactured to replace non-ferrous metals such as steel, aluminum and copper; The adhesive made by adding this product and curing agent into epoxy resin is often used for bonding and assembly of electronic instrument components, bonding between metal and porous materials, emergency repair, etc. it can also be used in the field of electronic ceramics. In the development of ceramic integrated electronic circuits, this product with medium viscosity and low hydroxyl is used as ceramic powder adhesive to increase the primary strength of ceramics.
Application field of polyvinyl butyral -- copper foil adhesive
Polyvinyl butyral (PVB) and phenolic resin cooperate to produce copper foil adhesive, which is used in the production of copper clad laminate. It has good peel strength and tin welding temperature resistance, and is widely used in various fields.
Application field of polyvinyl butyral - self adhesive enamelled wire paint
Polyvinyl butyral is the main raw material of self-adhesive enamelled wire paint. After the enameled wire is wound and formed in the electrodes of motors, electrical appliances and instruments, as long as it is heated for several minutes at a certain temperature or treated with appropriate solvent, the coils can be bonded together by themselves without impregnation and drying.
This work confirms previous studies that show P-25 and other untreated anatase 377 nanoparticles should not be employed in sunscreens because the toxicity of P25TiO2NPs under UV radiation is significant.
Titanium dioxide as used in sunscreens is commonly modified with other ingredients to ensure efficacy and stability. Examples of what are known as surface modifier ingredients used for titanium dioxide include stearic acid, isostearic acid, polyhydroxystearic acid, and dimethicone/methicone copolymer.
In recent decades, concerns for the risks of titanium dioxide consumption have grown.
Characteristics of Common White Pigments