The vitaminC@P25TiO₂NPs, on the other hand, were obtained through an optimized method based on Mallakpour et al. [27]. Initially, 0.02 g of P25TiO₂NPs were dispersed in 1 mL of ultrapure water and stirred in a Vortex. Next, 100 μL of HCl (0.01 M) were added (pH 2) to 100 uL of P25TiO₂NPs to avoid gel formation. Then, 100 μL of vitamin C dissolved in ultra-pure water (5.0 × 10⁻³ M) solution were added to the mixture and was ultrasonicated for 30 min. Finally, vitamin C was added in excess to gain a beige-orange color suspension, and the ultrasonication continued for another 30 min. The pellet obtained after centrifuging the suspension for 10 min at 4500 rpm was resuspended in ultrapure water, centrifuged again, and then lyophilized.

The morphology of vitaminB2@P25TiO₂NPs is coherent with the description of Degussa P25 typical population. Size distribution histograms were made from manual measures of the nanoparticles observed in SEM micrographs using ImageJ®. This data showed that more than 70% is anatase (between 20 and 60 nm) with a minor amount of rutile characteristic bars (between 80 and 100 nm) and a small amount of amorphous phase (<40 nm) [36]. Further analysis of the same sample areas with an EDS probe demonstrated the presence of organic material composed of C and O (Fig. 2). This material was found homogeneously distributed on the surface of the different shapes of P25TiO₂NP, not in the background, indicating a specific interaction that could be attributed to the functionalization of the P25TiO₂NPs with vitamin B2.

Store in a cool, ventilated, dry warehouse. Should pay attention to heat and moisture. Store separately from acid products. Lightly load and unload during handling to prevent damage to the packaging. Packed in woven bags lined with polyethylene plastic bags, each bag has a net weight of 25kg. In case of fire, use water and various fire extinguishers to save.