Defects such as surface film and surface inclusions can be found and treated by conventional techniques in order to remove them locally from the surface of the deposition layer. Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank.

Most people in addition to pay attention to the price of barbed rope, many people for hot-dip galvanized barbed rope or cold galvanized barbed rope will have questions, in fact, these two products, the price difference is not very big, so how to choose hot-dip galvanized barbed rope and electric galvanized barbed rope?

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

Cold wire drawing is mainly used in the production of hardened low carbon steel wire, with a diameter of 8 mm steel bar to play a fixed role in the development of the construction industry has played a role in promoting the development of the construction industry, widely used. The bonding and anchorage performance between cold wire drawing and concrete is good. When used in components, the phenomenon of cracking in the anchorage area of components and damage caused by steel wire slip is fundamentally eliminated, and the bearing capacity and anti-cracking capacity of the end of components are improved.

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.