When the coating of large galvanized wire is blistered in the process of galvanizing, the bath temperature should be checked first. If the bath temperature is not low, and then strengthen the removal of oil before plating, to prevent the base metal in acid corrosion. If you pay attention to these problems, the bubbling phenomenon still exists, it should pay attention to the dosage and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, to reduce the content of additives, observe whether the bubbling phenomenon is improved. If there is no improvement, check whether the additive has been stored for too long or whether it contains too many impurities.

3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag

Each coil of steel wire shall consist of one wire. The surface of the rod shall not have cracks, folds, scars, ears, layers or inclusions. However, indentation, pits, bumps, scratches and pockmarks are allowed, and the depth or height shall not be 0.2mm. There should be no corrosion and oxidation skin on the surface of the steel wire, and oxidation color is allowed by heat treatment. The surface of the wire is allowed to have scratches not exceeding half of the allowable deviation range of the diameter, and local defects not exceeding the allowable deviation of the appropriate diameter.

Common galvanized iron wire equipment is usually used in barbecue net, barbecue net generally requires to have a long service life, with galvanized iron wire equipment to wire a layer of zinc, barbecue net is not easy to be corroded.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging treatment.

The thorn rope belongs to the weaving industry, so it is less affected by environmental protection. The thorn rope will not be discarded in the production process, and it belongs to the weaving industry, so the situation is less affected by environmental protection.

5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.