The natural barite containing more than 95% of barium sulfate is mixed with anthracite in a ratio of 3:1 (mass), and is pulverized to a diameter of about 2 cm or less to enter a reduction furnace, and the front stage of the furnace temperature is controlled by 1000 to 1200 ° C, and the latter stage is 500 to 600 ° C, the reduction furnace rotates at a speed of 80s per revolution, the reaction conversion rate is 80% to 90%, the obtained barium sulfide enters the leaching device, the control temperature is above 65 ° C, and the content of barium sulfide is 701%, and then enters the clarification. The barrel is clarified and then added with zinc sulfate to control the zinc sulfate content to be greater than 28%, and the pH is 8-9, and a mixture of barium sulfate and zinc sulfide having a density of

...
...

Various titanium-rich minerals, including ilmenite and rutile, can serve as starting materials for the production of highly purified Titanium Dioxide. The predominant method employed in Titanium Dioxide production is the chloride process. In this process, the mineral, along with coke and chlorine, undergoes a reaction within a fluidized bed, resulting in the formation of primarily titanium tetrachloride and carbon dioxide. Subsequently, the titanium tetrachloride undergoes purification and conversion to Titanium Dioxide. Another method involves treating ilmenite with sulfuric acid to manufacture the chemical.

...