Sulphate process. The ilmenite is reacted with sulphuric acid giving titanium sulphate and ferric oxide. After separation of ferric oxide, addition of alkali allows precipitation of hydrous titanium dioxide. The washed precipitate is calcined in a rotary kiln to render titanium dioxide. The nucleation and calcination conditions determine the crystalline structure of titanium dioxide (e.g. rutile or anatase).

Lithopone, C.I. Pigment White 5, is a mixture of inorganic compounds, widely used as a white pigment powder. It is composed of a mixture of barium sulfate and zinc sulfide. These insoluble compounds blend well with organic compounds and confer opacity. It was made popular by the cheap production costs, greater coverage. Related white pigments include titanium dioxide, zinc oxide (zinc white), zinc sulfide, and white lead.^[1]

2. Barite calcination method A solution of barium sulfide is prepared. The sulfuric acid and zinc oxide are reacted, purified by adding potassium permanganate and zinc powder, and compressed to obtain a zinc sulfate solution. Then, the prepared barium sulfide solution is mixed and subjected to a metathesis reaction to obtain a mixture of zinc sulfide and barium sulfate, and then the precipitate is subjected to pressure filtration, calcination, wet grinding, drying, and pulverization to obtain a zinc white product.