As awareness of the environmental consequences associated with industrial activities heightened, TiO2 industry factories began to adopt cleaner production technologies. Innovations such as the chloride process offered not only improved yields but also reduced energy consumption and waste generation. Moreover, the introduction of advanced filtration systems and waste treatment protocols significantly mitigated the environmental impact of TiO2 manufacturing.

...



Application:
1. Due to its rheological and optical properties, Lithopone offers technical and economic advantages wherever organic and inorganic resin systems need to be relatively highly pigmented for specific applications. Lithopone has therefore traditionally been used in putties, mastics, jointing and sealing compounds, primers, undercoats and marking paints. In powder coatings it is possible to replace TiO2 partially, very economically.

2. The low Mohs' hardness of Lithopone leads to low abrasiveness in comparison with TiO2.

3. Lithopone 30 % (= 30% zinc sulfide share) is proven to be of particular use as a TiO2 Substitute in thermoplastic masterbatches. Even at very high pigment loadings it disperses easily. A masterbatch containing 50 % TiO2 and 25 % Lithopone 30 % DS has the same hiding power as one containing 60 %TiO2. Cost savings are strongly related to the price ratio of Lithopone and TiO2 and the price of for example polyethylene or polypropylene.

4. The Lithopone batch has a much higher extrusion rate too. Furthermore the impact strength of many thermoplastics such as PP and ABS can be noticeably improved by using Lithopone as a TiO2 substitute. Generally spoken, Lithopone can be used at loadings up to 80 % by weight without causing polymer breakdown

...

The natural barite containing more than 95% of barium sulfate is mixed with anthracite in a ratio of 3:1 (mass), and is pulverized to a diameter of about 2 cm or less to enter a reduction furnace, and the front stage of the furnace temperature is controlled by 1000 to 1200 ° C, and the latter stage is 500 to 600 ° C, the reduction furnace rotates at a speed of 80s per revolution, the reaction conversion rate is 80% to 90%, the obtained barium sulfide enters the leaching device, the control temperature is above 65 ° C, and the content of barium sulfide is 701%, and then enters the clarification. The barrel is clarified and then added with zinc sulfate to control the zinc sulfate content to be greater than 28%, and the pH is 8-9, and a mixture of barium sulfate and zinc sulfide having a density of

...