Stainless steel blade barbed wire production process is similar to galvanized blade barbed wire production process, usually according to the mold to determine the size of the blade.

The advantage of galvanized iron wire after annealing: after annealing increases the elongation of the iron wire. Makes the product softer and increases the range of application. After electric galvanizing hot dip galvanizing. Copper electroplating is widely used and screen production. Galvanized iron wire is a soft iron wire product processed by low carbon steel wire through cold drawing, heating, constant temperature, and even heat preservation. Generally, the quality of ordinary galvanized iron wire will be relatively soft, the softness is relatively balanced, and the color is consistent. It is mainly used in construction, mining, chemical industry and so on.

If it is not packaged, then a car of blade thorn rope can not be loaded with many pieces, and it is also relatively occupied and easy to lose in the transportation process. The number of the packed blade thorn rope is 50 bundles, and the volume is reduced after hydraulic compression so that it is more convenient to load and unload, and the forklift can easily load and unload. Under normal circumstances, when exporting, the blade thorn rope will be packaged and sold, so that the volume occupied in the container is relatively small, which can be easily placed and will not occupy much place.

Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

6, according to the wire diameter thickness to adjust zinc dipping time. Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is the length of the distance between the lead screw on the zinc pot and the ceramic sinking roll. The zinc dipping time of coarse wire diameter should be long, and the zinc dipping time of fine wire diameter should be short.