The common weight standard of galvanized barbed rope is 25kg per coil, and the length of each coil varies from 220-250 meters according to the specifications of the barbed rope. And of course we all know that the heavier the disc the longer it is. But there is one point that is worth our attention, that is, the hollow inside the general larger disk is relatively small, and the hollow inside the lighter galvanized thorn rope is relatively large. The purpose of this is to reduce the number of bending of the thorn rope and make it easier and more beautiful when installing, on the other hand, it looks larger in appearance.

A. When the thickness of the plating is 3-4 mm, the zinc adhesion should be less than 460g/m, that is, the average thickness of the zinc layer is not less than 65 microns.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

2, mesh, mesh also directly affect the price of stone cage net

In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

Now many hardware manufacturers produce iron wire, and iron wire is very easy to rust, if you need to use in outdoor or humid places, generally customers will require the use of galvanized iron wire equipment to give the wire a layer of zinc, the thickness can be determined according to user requirements. Galvanized iron wire equipment is specially used for the plating of iron. Generally speaking, the stability of zinc is much higher than that of iron, and it will not rust in the daily water vapor or damp place.

There are still some differences between the welding mesh and the wire mesh and the steel mesh. This mesh is mainly a welding mesh made of high quality low carbon steel wire straightened and cut, and then welded with electric welding equipment. It can be said that because of the characteristics of fast production and convenient transportation, it has been applied to many industries. The application of welding mesh in the industry, because the mesh has strong corrosion resistance and uniform mesh. It has become a special grid for floor heating in the building industry and has been applied in many fields.

Dip plastic six side barbed wire corrosion lost the original characteristics, in the shape, color and mechanical properties and other aspects will change, resulting in equipment damage, pipeline leakage, in particular, is prone to fracture, lose the original protective function.

The production process is to roll the hot metal billet into 5mm thick steel, and then put it into the wire drawing device, draw into different diameters of the line and gradually reduce the aperture of the wire drawing disk. Production process through cooling, annealing, coating and other processing technology, and then made into a variety of different specifications of galvanized wire. Galvanized wire production because of simple process, wide application, early development. Galvanized wire or steel wire is a cold working product of steel wire, and the material used is generally low carbon steel or stainless steel.

In moist air, a dense basic zinc carbonate film forms on the surface of zinc. Zinc coating belongs to the anodic coating, it is mainly used to prevent the corrosion of steel, its protective performance and the thickness of the coating is very important. The protective and decorative properties of zinc coating can be improved significantly after passivation treatment, dyeing or coating with light protection agent.