The galvanizing process of galvanized wire products is a very effective metal anticorrosion method. It is also widely used in other industrial fields. The use of galvanized iron wire is very common in metal structure equipment of various industries. Due to the influence of production technology or other factors, the zinc layer of galvanized wire products will be different to a certain extent, especially ordinary galvanized can not reach the beauty of electric galvanized, the zinc layer of ordinary galvanized wire is mainly for corrosion prevention.

Pet cage is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welding, which is characterized by beautiful, lightweight, folding, easy to store. The surface treatment of pet cage is generally: cold galvanized, hot galvanized, spray, dip, chromium plating, nickel plating and other methods.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

6, passivation to remove hydrogen parts should be passivation after the removal of hydrogen, passivation before the application of 1%H2SO4 or 1% hydrochloric acid activation 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

Although galvanized iron wire has the protection of galvanized layer, it does not say that it will not rust at all, but delays the time of rust. In general, cold galvanized iron wire can be kept for 1-2 years without rust, hot galvanized iron wire can be used for 8-10 years without rust. If properly maintained, the use time will be longer. So how to prevent galvanized iron wire rust?

3, with oil cloth (oil used cloth), carefully from inside to outside, including each cage wire repeatedly grinding many times. The front of the bird cage, the door flowers, where vision is often in place, are repeatedly rubbed in order to improve the surface finish, equivalent to “grinding”. Note: door flowers, arhat lines and other structures are delicate and fragile, do not break. This process, which requires time and patience, care, is also a process of observing and appreciating the cage. Use new cloth again, according to the above process, wipe again and again. This process is equivalent to polishing. For important parts, you can use a little force, the speed can be a little faster (do not use force). Be careful to fold the cloth neatly, otherwise marks will easily form. When this process is complete, the surface finish is significantly improved.

The shape of the cage has round, square, octagonal, hexagonal and other shapes. Because the circular space uses a large area, it is more suitable for the activities of birds, and it is not easy to get hurt, so it is popular with everyone. A cage is dear to a man who loves birds, for it is inhabited by his master’s birds. If well maintained, it can be maintained for many years. Let’s look at how to maintain the cage.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.