Because the coating obtained is thicker, hot-dip galvanizing has very good protective function than electric galvanizing, so it is an important maintenance coating for iron and steel parts in strict working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transportation, shipbuilding and other occupations. In the field of agriculture, such as pesticide irrigation, greenhouse and construction industry such as water and gas transportation, wire casing, scaffolding, Bridges, highway guardrail and other aspects, it has been widely used in these years.

Friends in the industry know that galvanized iron wire has two kinds of cold galvanized iron wire and hot galvanized iron wire, so what is the difference between cold galvanized iron wire and hot galvanized iron wire? Which is good?

Electrode application range is wide, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding. (1) Welding between low carbon steel, low alloy steel, medium carbon steel, alloy steel and other metal materials or dissimilar metal materials can be achieved. The weld has good comprehensive mechanical properties, and the tensile strength can reach more than 400MPa. ⑵ Can realize the welding of large plate, steel frame, plate – tube, rod – rod, tube – tube and other profiles. ⑶, can realize docking, Angle, lap, T joint and other joint forms of welding. ⑷ mainly suitable for flat welding.(5) it can surfacing the parts of wear failure, so as to obtain the surface surfacing layer with melting depth, smooth surface and excellent performance. ⑹ It can be realized that no bevel 1 ~ 6mm thick metal sheet single-side welding double-side molding.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.