The characteristics of these cages are small, light, easy to carry and easy to clean. For small animal cage, the wire diameter of the general iron wire is not very large, the thickness of the plastic is relatively thin, so the use of the time can not be “violence”, otherwise the cage in the “destruction” will occur under the welding or plastic crack.

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

Bridge protection system generally do not need to be specially installed special drainage system, the use of hexagonal mesh made of gabion mesh box, the inside of the filler are selected stones, these stones are not easy to wear, and between the stones and stones will retain some gaps, so it is very good to meet the drainage requirements.

The diameter of cold-drawn wire should conform to the contract, check whether the amount of zinc meets the requirements of the contract, check the tensile strength, and ask the factory to provide the corresponding inspection report. The wire factory introduces that the weight of a single coil of wire of different specifications should not be lower than the volume weight required by the contract, and record the value. No contacts are generated for each reel of wire. If there are contacts, no more than three contacts are generated for each reel. Each contact should be smooth surface treatment, the wire can not be pulled off from the contact, in line with customer packaging requirements.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

Annealed wire is mainly made of soft iron wire through low carbon steel heating, hot drawing, constant temperature and other processes. Because of the differences in use, there are also different in the production process, and the specifications are varied. Annealed wire can be widely used, mainly because annealed wire and other kinds of wire, has many advantages.

There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.