When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

1. Zinc pot operators must stick to their posts

5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.

Since galvanized iron wire will rust, we need to pay attention in the process of storage and use, try to store in a dry and ventilated environment, in the process of use to avoid damaging the surface of galvanized iron wire, we can slow down the time of galvanized iron wire rust.

In the purchase of large rolls of galvanized wire, see the hardness of galvanized wire first, only after the hardness reaches the standard can be used. The hardness standard of large roll galvanized wire is a very important performance index and an economic test method. But for the hardness of metal materials, there is not a unified and clear definition including all test methods at home and abroad.

Razor blade barbed rope has been widely used in military sites, prisons, government agencies, banks in the world. The walls of living quarters, private homes, villas, fences, doors and Windows, highways, railway guardrail and border lines and other protection and security.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

In order to improve the corrosion resistance of steel pipe, the general steel pipe is galvanized. Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.