There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.

Maintenance is indispensable in the use of galvanized wire. Large coils of galvanized silk should be coated with oil, fiber core immersion oil, oil is required to protect the fiber core is not rotten, not rust, wire moisture fiber, and from the internal lubrication wire rope. Surface coating so that all wire rope strands in the surface, are evenly coated with a layer of rust-proof lubrication grease, which for friction lifting and mineral water large mine rope, to be coated with grinding and water-resistant black oil grease. Coated with red oil with strong film and good rust resistance, it is required to have a thin oil layer, which is easy to keep clean during operation.

Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.

Surface coating, surface inclusion and other defects can be removed locally from the surface of the deposited layer before galvanized, which can be found and treated by conventional techniques. Excess foam is caused by the introduction of soap and saponable fatty surfactants into the tank. Moderate foam formation rates may be harmless. The presence of a large number of tiny homogenous particles in the tank, which can stabilize the foam layer, mat with activated carbon to remove surface active substances, or make the foam less stable through filtration, are effective measures.

5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

Greenhouse steel pipe is mainly made of greenhouse composite materials made of pull rod, pressure rod, column, and arch rod to cover the plastic film in a greenhouse. Wire factory introduces its this shape is circular plastic greenhouse, this greenhouse covers a large area, the effect of heat absorption is also very good, convenient to build, the cost of building a is also very low. The raw material source of greenhouse steel pipe is very rich and extensive, and the application effect is good.