The natural barite containing more than 95% of barium sulfate is mixed with anthracite in a ratio of 3:1 (mass), and is pulverized to a diameter of about 2 cm or less to enter a reduction furnace, and the front stage of the furnace temperature is controlled by 1000 to 1200 ° C, and the latter stage is 500 to 600 ° C, the reduction furnace rotates at a speed of 80s per revolution, the reaction conversion rate is 80% to 90%, the obtained barium sulfide enters the leaching device, the control temperature is above 65 ° C, and the content of barium sulfide is 701%, and then enters the clarification. The barrel is clarified and then added with zinc sulfate to control the zinc sulfate content to be greater than 28%, and the pH is 8-9, and a mixture of barium sulfate and zinc sulfide having a density of

One of the key challenges facing TiO2 industry suppliers is the fluctuation of raw material prices. The production of TiO2 requires raw materials such as ilmenite or rutile, which are subject to market price volatility. Suppliers must carefully monitor these fluctuations and adjust their production processes accordingly to ensure profitability.

Although barium sulfate is almost completely inert, zinc sulfide degrades upon exposure to UV light, leading to darkening of the pigment. The severity of this UV reaction is dependent on a combination of two factors; how much zinc sulfide makes up the pigments formulation, and its total accumulated UV exposure. Depending on these factors Lithopone B301, Lithopone B311 powder itself may vary in shade over time, ranging from pure white all the way to grey or even black. To suppress this effect, a dopant might be used, like small amount of cobalt salts, which would be added to the formulation. This process creates cobalt-doped zinc sulfide. The cobalt salts help to stabilize zinc sulfide so it will not have as severe a reaction to UV exposure.

Those scientists found that sunscreen residue on the roof installers fingertips were being transferred to the colour bond sheets during installation & with titanium dioxide’s photo-sensitivity & the lovely sun’s help, the paint was literally peeling off those roofs.