In the purchase of barbed rope should be customer demand, so the amount of galvanized is different, then the two kinds of barbed rope and what is the difference, some customers need high zinc blade barbed rope, but high zinc blade barbed rope price to ordinary galvanized barbed rope price is more than 1000 yuan per ton, the two kinds of barbed rope products, the former is used in many aspects, such as the military, the government’s barbed rope, The latter is more for civilian use.

The steel mesh is also called longitudinal reinforcement and transverse reinforcement. The longitudinal reinforcement and transverse reinforcement are spaced at right angles to each other, and all the crossing points are welded together. It has the characteristics of crack – proof, small error and good quality. Steel mesh is mainly used in coal mine roadway, concrete pavement, bridge deck, airport runway and buildings. So, what are the advantages of mesh?

Many customers are in great need of galvanized barbed rope when they decide to purchase it, and the barbed rope specification determines the length of the later installation.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

Welding electrode has a wide range of applications, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding.

Thorn rope factory can not only have one type of product when processing thorn rope, a variety of models can meet the protection needs of different customers.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.

Spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and resistance to impact and oscillation. The strength and endurance objectives, especially to prevent the occurrence of modification cracks, are the key to the consumption of spring wire. The inner quality and outer quality of the wire rod directly affect the function of the wire.