The vitaminB2@TiO₂NPs were obtained at room temperature, by a method developed after trying several ratios of reactants. Briefly, 0.02 g of P25TiO₂NPs were dispersed in 1 mL of ultra-pure water and stirred in a Vortex. Next, 200 μl of vitamin B2 dissolved in ultra-pure water (5.3 × 10⁻³ M) were added to 200 μL of P25TiO2NPs and the mixture was ultrasonicated for 1 hour to achieve a deep-yellow homogeneous suspension. The pellet obtained after centrifuging the suspension for 10 min at 4500 rpm was resuspended in ultrapure water, centrifuged again, and then lyophilized.

Background 

Thermogravimetric analysis (TGA) was conducted in a sample of vitaminB2@P25TiO₂NPs using a TA-THA Q5000 equipment. Temperature ramp rate: 10 °C/min, maximum temperature: 1000 °C, under air. Part of the same sample was mounted on conductive copper tape grids and observed through a Carl Zeiss Sigma scanning electron microscope (SEM) with an EDS probe, at the “Laboratorio de Microscopía y Análisis por Rayos X” (LAMARX) of National University of Córdoba (Argentina).