Hot dip galvanized hexagonal net is made of low carbon steel wire by mechanized braided welding and then by hot dip zinc treatment. The net color is white and shiny, thick zinc layer, uniform mesh, flat mesh surface, solder joint tension resistance, high corrosion resistance. The surface of the steel wire is usually protected by hot-dip galvanizing, and the thickness of the galvanized protective layer can be made according to the requirements of customers. Hot-dip galvanizing hexagonal net is another kind of twisting mesh corresponding to the galvanizing hexagonal net.

Open pit coal mine due to poor air quality, a variety of harmful heavy metals are also more, so the corrosion strength of barbed rope products is particularly large, when using galvanized barbed rope must choose hot plating or plastic coated galvanized barbed rope, although the price is slightly higher, but in the long term development is more appropriate. Besides, when the barbed rope is installed near the coal mine, the pile foundation should be fixed to prevent the barbed rope from falling down due to soil erosion, thus losing the protective effect.

If the blade barbed rope produced by the barbed rope factory wants to be made into a straight line, it can’t be made too long because of the constraints of logistics.

Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.

The more turns thorn rope, at the same time will shorten some use the length, but its tensile strength is improved and barbed wire manufacturer production products general laps for the 3 ring, very few customers to use the product requires 5 laps, this time both in processing fees and use the length is calculated need extra.

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

Some customers are more concerned about the quality of the problem, so for the service life is more important, thorn rope factory will generally recommend the use of high zinc thorn rope or stainless steel thorn rope.

Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.