The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Galvanized iron wire will rust, mainly and the thickness of galvanized layer and the use of the environment, galvanized iron wire is also divided into cold galvanized iron wire and hot galvanized iron wire, in general, hot galvanized iron wire galvanized layer is thicker, rust prevention time is longer, generally can be 7 or 8 years without rust. If the galvanized layer is damaged, or long-term use in a humid environment, it will accelerate the rust time of galvanized iron wire.

Zinc is a silver-white metal, brittle at room temperature, soluble in acid and alkali, known as amphoteric metal. Pure zinc is more stable in dry air, and small in humid air or water containing carbon dioxide and oxygen. A thin film layer of basic zinc carbonate will be formed on the surface, which can delay the corrosion rate of zinc layer. The corrosion resistance of galvanized layer in aqueous solution of acid, alkali and sodium chloride is relatively strong. It is also not resistant to corrosion in atmospheres containing carbon dioxide and hydrogen sulfide and in Marine atmospheres; In high temperature and high humidity air and containing organic acid atmosphere is small, galvanized layer is also easy to be corroded.

Hook mesh is woven with silk core hook, the mesh is uniform, flat, beautiful and generous net width, thick wire diameter, not easy to corrosion, long life, simple weaving, beautiful and useful. It is widely used to raise chickens, ducks, geese, rabbits and zoo pens. Mechanical equipment protection, highway guardrail, sports venues purse Seine, road beautification with protective net. The screen in the manufacture of a box shaped container, filled with stone cage, can be used to maintain and support the seawall, hillside, road and bridge, reservoirs and other civil engineering.