In the context of titanium dioxide determination, the process generally begins with the sample preparation, where a known mass of the sample containing TiO2 is dissolved or digested appropriately. The subsequent steps involve adding a precipitating agent, such as ammonium sulfate or sulfuric acid, to the prepared solution, which facilitates the formation of a titanium precipitate. This precipitate is often titanium hydroxide, which is not only insoluble but can be easily filtered out from the liquid phase.

In 1970, Japanese scholars studied the phase diagram of iron oxide microcrystalline formation, which laid a theoretical foundation for the preparation method of iron oxide yellow crystal seed. According to the research results, iron yellow crystal seeds can be formed under acidic or alkaline conditions. Because iron yellow is a crystal structure, in order to crystallize into pigment particles, it must first form crystal nucleus and become crystal seed, and then the crystal nucleus grows into iron yellow. Otherwise, only thin and dim color paste can be obtained, which does not have pigment properties. Acid process can be divided into iron sheet process and drop addition process.